| TYPICAL PROPERTIES OF Torlon® 5030 |
|
| |
|
Typical
Values(1) |
|
|
|
| |
Test |
U.S.
Customary Units |
SI
Units |
|
|
|
| Property |
Method(2) |
|
Value |
Units |
|
Value |
Units |
|
| Mechanical |
|
| Tensile strength |
|
|
| -321°F (-196°C) |
D 1708 |
|
29.5 |
kpsi |
|
204 |
MPa |
| 73°F (23°C) |
D 1708 |
|
29.7 |
kpsi |
|
205 |
MPa |
| 275°F (135°C) |
D 1708 |
|
23.1 |
kpsi |
|
160 |
MPa |
| 450°F (232°C) |
D 1708 |
|
16.3 |
kpsi |
|
113 |
MPa |
| Tensile elongation |
|
|
| -321°F (-196°C) |
D 1708 |
|
4 |
% |
|
4 |
% |
| 73°F (23°C) |
D 1708 |
|
7 |
% |
|
7 |
% |
| 275°F (135°C) |
D 1708 |
|
15 |
% |
|
15 |
% |
| 450°F (232°C) |
D 1708 |
|
12 |
% |
|
12 |
% |
| Tensile modulus |
|
|
| 73°F (23°C) |
D 1708 |
|
1560 |
kpsi |
|
10.8 |
GPa |
| Flexural strength |
|
|
| -321°F (-196°C) |
D 790 |
|
54.4 |
kpsi |
|
381 |
MPa |
| 73°F (23°C) |
D 790 |
|
48.3 |
kpsi |
|
338 |
MPa |
| 275°F (135°C) |
D 790 |
|
35.9 |
kpsi |
|
251 |
MPa |
| 450°F (232°C) |
D 790 |
|
26.2 |
kpsi |
|
184 |
MPa |
| Flexural modulus |
|
|
| -321°F (-196°C) |
D 790 |
|
2040 |
kpsi |
|
14.1 |
GPa |
| 73°F (23°C) |
D 790 |
|
1700 |
kpsi |
|
11.7 |
GPa |
| 275°F (135°C) |
D 790 |
|
1550 |
kpsi |
|
10.7 |
GPa |
| 450°F (232°C) |
D 790 |
|
1430 |
kpsi |
|
9.9 |
GPa |
| Izod impact strength |
|
|
| Notched |
D 256 |
|
1.5 |
ft-lb/in |
|
79 |
J/m |
| Unnotched |
D 256 |
|
9.5 |
ft-lb/in |
|
504 |
J/m |
| Shear strength |
D 732 |
|
20.1 |
kpsi |
|
140 |
MPa |
| Compressive strength |
D 695 |
|
38.3 |
kpsi |
|
260 |
MPa |
| Compressive modulus |
D 695 |
|
1150 |
kpsi |
|
7.9 |
GPa |
| Poisson's ratio |
|
|
0.43 |
|
|
0.43 |
|
|
| Thermal |
|
| Heat deflection temperature |
|
|
| at 264 psi (1.82 MPa) |
D 648 |
|
539 |
°F |
|
282 |
°C |
| Flammability Rating(3) |
UL-94 |
|
94 V-0 |
|
|
94 V-0 |
|
| Coefficient of thermal expansion |
D 696 |
|
9 |
10-6 in/in/°F |
|
16.2 |
10-6 m/m/°C |
| Thermal conductivity |
C 177 |
|
2.5 |
Btu-in/hrft2°F |
|
0.37 |
W/mK |
| Oxygen index |
D 2863 |
|
51 |
% |
|
51 |
% |
|
| Electrical |
|
| Dielectric strength |
D 149 |
|
840 |
V/mil |
|
32.6 |
kV/mm |
| Dielectric constant |
|
|
| at 1 kHz |
D 150 |
|
4.4 |
|
|
4.4 |
|
| at 1 MHz |
D 150 |
|
4.2 |
|
|
4.2 |
|
| Dissipation factor |
|
|
| at 1 kHz |
D 150 |
|
0.022 |
|
|
0.022 |
|
| at 1 MHz |
D 150 |
|
0.050 |
|
|
0.050 |
|
| Surface resistivity |
D 257 |
|
1x1018 |
ohm |
|
1x1018 |
ohm |
| Volume resistivity |
D 257 |
|
6x1016 |
ohm-in |
|
2x1015 |
ohm-m |
|
| General |
|
| Moisture absorption |
D 570 |
|
0.24 |
% |
|
0.24 |
% |
| Rockwell hardness |
D 785 |
|
94 |
|
|
94 |
|
| Density |
D 1505 |
|
0.058 |
lb/in3 |
|
1.61 |
g/cm3 |
|
| |
| 1Actual properties of individual batches will vary within specification limits. |
| 2Test methods are ASTM unless otherwise noted. |
| 3These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
|